Sheet, strip 9xvg - 100MnCrW4 - 1.2510
International Equivalent
| Mark | Analogue | W. Nr. | Aisi Uns | En | Order |
|---|---|---|---|---|---|
| 9HVG | 1.2510 | 100MnCrW4 | Delivery from the stock, in stock |
Evek GmbH offers to buy sheets and strips made of tool alloy steels 9XVG, 100MnCrW7 (1.2510) at a favorable price from the manufacturer. Supplier guarantees strict compliance with the range of profiles of products, provides timely delivery of rolled sheet to the address specified by the customer.
Chemical composition
Tool alloy steel 9XVG deep hardenability in the CIS countries is produced in accordance with the technical standards
- Carbon, % - 0,85...0,95;
- Silicon, % - 0,15...0,35;
- Manganese, % - 0,90...1,20;
- Chrome, % - 0,50...0,80;
- Tungsten, % - 0,50...0,80.
GOST allows the presence of titanium (not more than 0.03%) and vanadium - not more than 0.05%. Also in the composition of steel 9HVG present metallurgical impurities - sulfur and phosphorus, the percentage of which can not be higher than 0.03%.
The closest foreign analogue of 9XVG steel is tool steel grade 100MnCrW7 (1.2510). It is produced in Europe under ISO 4957 and in the US under ASTM A681. The composition of this steel is described in the following pages:
| Element | Carbon | Silicon | Manganese | Chrome | Vanadium | Tungsten |
|---|---|---|---|---|---|---|
| Content in steel, % | 0,85...1,00 | 0,10...0,50 | 1,00...1,40 | 0,40...0,70 | up to 0.30 | 0,40...0,60 |
Steel 100MnCrW7 (1.2510) may contain molybdenum, while the percentage of non-metallic impurities - phosphorus and sulfur - should not be more than 0,030%.
Company Evek GmbH realizes at advantageous price from the manufacturer of the sheet and strip, which are made of tool steel grades 9ХВГ and 100MnCrW7 (1.2510). Supplier provides timely delivery of rolled sheet to the point specified by the consumer.
Properties and application
Steels 9XVG and 100MnCrW7 (1.2510) are referred to a group of steels used for production of cutting and measuring tools. Steels can be subjected to various modes of hardening heat treatment for different hardness, forging and hot forging are possible at temperatures of 960...10000 C.
The main physical and mechanical properties of the steels under consideration after their hardening and tempering:
- Ultimate strength, MPa - 2150...2200;
- yield strength, MPa - 1350...1500;
- Young's modulus, GPa - 175...185;
- Hardness, HRC - 55...62;
- Brinell hardness after rolling, HB - 190.
Buy a cost-effective price from the manufacturer, sheet and strip, which are made of tool alloy steels brands 9XVG and 100MnCrW7 (1.2510), offers the company Evek GmbH. The supplier guarantees the conformity of dimensions and profiles of rolled sheets, ensures their timely delivery to the point specified by the customer.