Sheet, tape 1.4724
International Equivalent
| Mark | Analogue | W. Nr. | Aisi Uns | En | Order |
|---|---|---|---|---|---|
| 10Х17СУ | 1.4713 | X10CrAl7 | Delivery from the stock, in stock |
Supplier
We offer to buy sheet, strip, 1.4724 from the warehouse of the supplier Evek GmbH. Full compliance with international quality standards. The supplier Evek GmbH offers to buy sheet, strip 1.4724, today's best price.
Technical characteristics
Stainless heat-resistant low-alloy steel of ferrite class X10CrAlSi13. The base of the alloy is iron: its proportion of about 83%. The composition is alloyed with chromium, manganese, aluminum. Impurities do not exceed 0.3%. Specific weight is 7.7 g/cm3. It is used in the production of pipes, pipe fittings, parts of boiler installations, working at t ° up to 850 ° C; Service life over 10000 hours. The temperature of intensive scale formation is above 900 °C.
EN 10095-1999percentage composition
| Fe | C | Si | Mn | P | S | Cr | Al | Impurities |
|---|---|---|---|---|---|---|---|---|
| base | ≤0.12 | 0.7 - 1.4 | ≤1 | ≤0.04 | ≤0.015 | 12 - 14 | 0.7 - 1.2 | ≤0.3 |
Mechanical Properties
sT - ultimate strength 450-650 MPa
sT - limit of proportionality (yield strength for permanent deformation) 250 MPa
d5 - Tensile elongation at break 13-15%.
HB - Brinell hardness 192 MPa
Analogues
| European Union | China | Poland | GOST | France |
|---|---|---|---|---|
| EN | GB | PN | GOST | AFNOR |
| X10CrAlSi13 | OCr13Al | H13JS | 10KH13SYU | Z13C13 |
Alloying has a multifaceted effect on steel quality. Chromium increases hardness and corrosion resistance. Manganese content above 1% increases hardness, impact strength, wear resistance. Aluminum increases processability, prevents rusting.
Buy, bargain price
Where to order stainless heat-resistant steel? We offer sheet, strip 1.4724, the price - does not include additional costs. In the segment of heat-resistant stainless steel, Evek GmbH is a profitable supplier.