Steel D

Designation

Name	The value
Designation GOST Cyrillic	Д
Designation GOST Latin	D
Transliteration	D
By chemical elements	Cu

Description

The steel D is used: for the production of billets of circular cross-section of steel treated liquid synthetic slag in the ladle and is intended for the production of seamless pipes gorjachedeformirovannye.

Standards

Name	Code	Standards
Blanks. Of the workpiece. Slabs	В31	TU 14-1-3500-82

Chemical composition

Standard	C	S	P	Mn	Cr	Si	Ni	Fe	Cu
TU 14-1-3500-82	0.41-0.78	≤0.015	≤0.04	0.65-0.9	≤0.3	0.17-0.37	≤0.3	Rest	≤0.25

Fe is the basis.
According to TU 14-1-3500-82 in the pipe blank, the content of residual elements in D grade steel should not exceed the requirements of GOST 380. In finished rolled products, tolerances in chemical composition should not exceed GOST 380 standards, with the exception of sulfur and phosphorus, in which deviations not allowed. The total content of sulfur and phosphorus should not be more than 0.050%.

Mechanical properties

Section, mm	s_T\|s_0,2, MPa	σ_U, MPa	d₅, %	KCU, kJ/m²
Tubular billet on the other 14-1-3500-82. Normalization
25	≥373	≥638	≥19	≥590

Description mechanical marks

Name	Description
s_T\|s_0,2	Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σ_U	Limit short-term strength
d₅	Elongation after rupture
KCU	Toughness

Technological properties

Name	The value
Macrostructure and pollution	The macrostructure of billets on the other 14-1-3500-82 shall conform to the requirements of OST 14-21-77. Contamination of metal non-metallic inclusions shall not exceed the maximum score: - sulphides (S) - 3.5 points; - on oxides and silicates (FROM, OS, SP, SH) - 4.0 points.