Steel 08ЮП

Designation

Name	The value
Designation GOST Cyrillic	08ЮП
Designation GOST Latin	08JuP
Transliteration	08YuP
By chemical elements	08AlP

Description

08ЮП steel is used: for the production of cold-rolled sheet and strip used for the production of parts by cold-forming.

Note

Steel low-carbon high tensile strength.

Standards

Name	Code	Standards
Sheets and strips	В33	TU 14-1-5296-2004

Mechanical properties

Section, mm	s_T\|s_0,2, MPa	σ_U, MPa	d
Rolled sheet and strip as supplied on the other 14-1-5296-2004 (δ in the graph set index δ80, samples with a length of 80 mm and a width of 20 mm transverse to the direction of rolling)
	220-280	340-410	≥31

Description mechanical marks

Name	Description
s_T\|s_0,2	Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σ_U	Limit short-term strength
d	Elongation after rupture

Technological properties

Name	The value
Macrostructure and pollution	The bundle of steel is not allowed.
Microstructure	Microstructure of rolled on the other 14-1-5296-2004 must be ferrite-cementite. The ferrite grains must be elongated, equiaxed allowed. Equiaxed microstructure with the grain size of the ferrite must comply with 7, 8, 9, 10 numbers according to GOST 5639. allowed the uneven grain of the ferrite within three interconnected rooms. Structurally-free cementite should be no more than 2 points In a row according to GOST 5640 (scale 1).
Particularities of production of goods	On the other 14-1-5296-2004 rolled thickness 2 mm and shall withstand the bend test at 180° to the contact without cracks and delaminations. A surface rental should be covered with a uniform layer of preservative oil in an amount of from 0.8 to 1.5 g/m2, neutral with respect to the surface of rolled products. Oil grade is agreed with the consumer.
Features of heat treatment	On the other 14-1-5296-2004 rental comes heat-treated and trained strength class 220.