| Name | The value |
|---|---|
| Name | The value |
| Designation GOST Cyrillic | 35НГМЛ |
| Designation GOST Latin | 35HGML |
| Transliteration | 35NGML |
| By chemical elements | 35НMnMo |
35NGML steel is used: for the production of castings for critical loaded parts, which are requirements of high strength and sufficient toughness, working under static and dynamic loads.
| Standard | C | S | P | Mn | Si | Ni | Fe | Mo |
|---|---|---|---|---|---|---|---|---|
| Standard | C | S | P | Mn | Si | Ni | Fe | Mo |
| GOST 977-88 | 0.32-0.42 | ≤0.04 | ≤0.04 | 0.8-1.2 | 0.2-0.4 | 0.8-1.2 | Rest | 0.15-0.25 |
| Section, mm | sT|s0,2, MPa | σU, MPa | d5, % | y, % | KCU, kJ/m2 | HB, MPa |
|---|---|---|---|---|---|---|
| Section, mm | sT|s0,2, MPa | σU, MPa | d5, % | y, % | KCU, kJ/m2 | HB, MPa |
| Hardening in air, 860-880 °C + vacation at 600-650 °C, air cooling | ||||||
| 100 | ≥589 | ≥736 | ≥12 | ≥25 | ≥392 | 217-262 |