Steel 04Х13Н4АГ20 (ЧС52)

  • Steel 12Х11В2МФ (ЭИ756)
  • Steel 08Х21Н6М2Т (EP54)
  • Steel 10Х12Н3М2ФА (ЦД-М)
  • Steel 10Х12НД (0Х12НД)
  • Steel 10Х13Г12БС2Н2Д2 (DI59)
  • Steel 10X18G14AN4 (EP197; X18G14AN4)
  • Steel 10Х32Н8 (EP263; Х32Н8)
  • Steel 10Х9МФБ (DI82)
  • 08X14F steel
  • Steel 12X13 (1X13)
  • Steel 12X18H10T (X18H10T)
  • Steel 12Х18Н12Т (Х18Н12Т)
  • 12X18H9SMR steel (EP414; Х18Н9СМР)
  • Steel 12Х18Н9Т (Х18Н9Т)
  • Steel 16Х20К6Н2МВФ (EP768; VNS-22)
  • Steel 19Х20Н4АМ3Д2С (EC7)
  • Steel 90G29Yu9VBM (DI38; 90G29Yu9VMBF; DI38F)
  • Steel 03Х24Н6АМ3 (ЗИ130)
  • Steel 015Х14Н19С6Б (ChS110)
  • Steel 015Х20Н25Г2Б (EP754)
  • Steel 02Х24Н6АМ3 (DI91)
  • Steel 03N18K9M5T (EP637; MS200)
  • Steel 03Х16Н15М3Б (026Х16Н15М3Б; ЭИ844Б)
  • Steel 03Х18Н9Т (Х18Н9Т)
  • Steel 03Х19Н15Г6М2АВ2 (ChS39)
  • Steel 03Х21Н32М3Б (EP864; ČS33)
  • Steel 08Х20Н5АГ12МФ (DI8)
  • Steel 03Х9К14Н6М3Д (EP921; 03Х9К14Н6М3ДФ)
  • Steel 04Х11Н9М2Д2 (EP832; 04Х11Н9М2Д2ТЮ)
  • Steel 04Х13Н4АГ20 (ChS52)
  • Steel 04Х14К13Н4М3ТВ (EP767)
  • Steel 05Х15Н9Г6АМ (ChS31)
  • Steel 05Х21Н12Г2БРч (DI94)
  • Steel 07X13AG20 (ChS46)

    • Designation

    Name The value
    Designation GOST Cyrillic 04Х13Н4АГ20
    Designation GOST Latin 04X13H4AG20
    Transliteration 04H13N4AG20
    By chemical elements 04Cr13Н4NMn20
    Name The value
    Designation GOST Cyrillic ЧС52
    Designation GOST Latin ChC52
    Transliteration ChS52
    By chemical elements ZrС52

    Description

    04Х13Н4АГ20 steel is used: for the production of hot rolled flats, intended for the manufacture of parts of power engineering and aerospace technology, operating at temperatures from -210 °C to +400 °C almost without limit resource exploitation.

    Note

    Vysokoorganizovannaja low carbon corrosion-resistant heat-resistant and heat-resistant austenitic steel.

    Standards

    Name Code Standards
    Sheets and strips В33 TU 14-1-2508-78

    Chemical composition

    Standard C S P Mn Cr Si Ni Fe N B Ca Ce
    TU 14-1-2508-78 ≤0.07 ≤0.025 ≤0.035 19-22 12-14.8 ≤0.6 3.8-5.3 Rest 0.08-0.18 ≤0.003 ≤0.1 ≤0.1
    Fe is the basis.
    According to TU 14-1-2508-78 cerium, boron and calcium are introduced into the steel by calculation and chemical analysis is not determined.