| Designation GOST Cyrillic | 10895 |
| Designation GOST Latin | 10895 |
| Transliteration | 10895 |
| By chemical elements | 10895 |
10895 steel is used: for magnetic circuits of electrical machines and devices.
Steel hot rolled and forged, undoped silicon without standardization of ageing coefficient, coercive force in open circuit ≤ 95 A/m.
| Name | Code | Standards |
|---|---|---|
| Name | Code | Standards |
| Bars and shapes | В22 | GOST 1133-71, GOST 2590-2006, GOST 2591-2006 |
| Sheets and strips | В33 | GOST 4405-75, TU 14-1-1189-74, TU 14-1-3070-80 |
| Bars and shapes | В32 | GOST 7417-75, GOST 11036-75, TU 14-11-245-88 |
| Blanks. Of the workpiece. Slabs | В31 | TU 14-1-3417-82 |
| Standard | C | S | P | Mn | Si | Fe | Cu |
|---|---|---|---|---|---|---|---|
| Standard | C | S | P | Mn | Si | Fe | Cu |
| GOST 11036-75 | ≤0.035 | ≤0.03 | ≤0.02 | ≤0.3 | ≤0.3 | Rest | ≤0.3 |
| σU, MPa | d5, % | y, % | HB, MPa |
|---|---|---|---|
| σU, MPa | d5, % | y, % | HB, MPa |
| Bars hot rolled and forged on delivery | |||
| ≥270 | ≥24 | ≥60 | ≤131 |
| Name | Description |
|---|---|
| Name | Description |
| σU | Limit short-term strength |
| d5 | Elongation after rupture |
| y | The relative narrowing |
| HB | Brinell hardness number |