Name	The value
Designation GOST Cyrillic	ЗлСрНЦМ 58,5-8-8,2-2,5
Designation GOST Latin	ZlCpHTsM 58,5-8-8,2-2,5
Transliteration	ZlSrNTsM 585-8-82-25
By chemical elements	AuAgNiZnCu 58,5-8-8,2-2,5

Name	The value
Designation GOST Cyrillic	ЗлСрНЦМ 585-80-82-25
Designation GOST Latin	ZlCpHTsM 585-80-82-25
Transliteration	ZlSrNTsM 585-80-82-25
By chemical elements	AuAgNiZnCu 585-80-82-25

Description

Alloy Slsmc 58,5−8-8,2−2,5 used: for the manufacture of jewelry for personal adornment (rings, rings, earrings, medallions, pendants, brooches, bracelets); Souvenirs (commemorative medals, signs, badges); articles for smokers (cigarette cases, cigarette holders, mouthpieces).

Note

Alloy 585-th sample is in shade of color to the group of white gold.

Standards

Name	Code	Standards
Non-ferrous metals, including rare, and their alloys	В51	GOST 30649-99, GOST Р 51152-98

Chemical composition

Standard	Ni	Fe	Cu	Zn	Sb	Pb	Bi	O	Ag	Au
GOST 30649-99	7.7-8.7	≤0.15	Rest	2.2-2.8	≤0.005	≤0.005	≤0.005	≤0.007	7.5-8.5	58.5-59

Au is the base.
According to GOST 30649-99 the chemical composition is given for the jewelry alloy YuZlSrNTSM 58,5-8-8,2-2,5 (ЮЗлСрНЦМ 585-80-82-25). The sum of the normalized impurities is ≤ 0.170%.

Physical characteristics

Temperature	r, kg/m³
20	13110

A description of the physical symbols

Name	Description
r	Density

Technological properties

Name	The value
Pressure treatment	Suitable for all types of cold treatment.
Features of heat treatment	The plastic alloy in the annealed condition. Not susceptible to hot cracking during annealing or soldering.
Casting	Suitable for all kinds of casting, including casting the caste under the gem-setting. The presence of graphite in the casting is undesirable because it causes brittleness of the alloy. The presence of zinc makes the alloy increases fluidity and sharper than cadmium lowers the melting point.

Alloy Slsmc 58,5-8-8,2-2,5 (Slsmc 585-80-82-25)

Designation