Designation
| Name |
The value |
| Designation GOST Cyrillic |
ХН60КМЮБВТФ |
| Designation GOST Latin |
XH60KMJuBBTF |
| Transliteration |
HN60KMYuBVTF |
| By chemical elements |
CrNi60CoCuAlBeВTeP |
| Name |
The value |
| Designation GOST Cyrillic |
ЭП962 |
| Designation GOST Latin |
EP962 |
| Transliteration |
EhP962 |
| By chemical elements |
- |
Description
Alloy ХН60КМЮБВТФ used: for the manufacture of various high-temperature sobotiste parts of power plant equipment.
Standards
| Name |
Code |
Standards |
| Processing of metals by pressure. Forgings |
В03 |
TU 14-1-2345-88 |
| Bars and shapes |
В32 |
TU 14-1-3362-81 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
Cu |
Al |
V |
B |
Ti |
Mo |
Nb |
W |
Zr |
Co |
| TU 14-1-3362-81 |
0.1-0.14 |
≤0.01 |
≤0.02 |
≤0.3 |
12-15 |
≤0.3 |
Rest |
≤1 |
≤0.07 |
3.1-4 |
0.1-0.5 |
≤0.01 |
2.4-3 |
4.2-5 |
3.1-3.7 |
2.4-3 |
≤0.06 |
9-12 |
Ni is the basis.
According to TU 14-1-3362-81, the chemical composition is given for an alloy of grades ХН60КМЮБВТФ-ИД (ЭП962-ИД) and ХН60КМЮБВТФ-ИЛ (ЭП962-ИЛ).
Mechanical properties
| sT|s0,2, MPa |
σU, MPa |
d5, % |
y, % |
KCU, kJ/m2 |
| Forgings (washers) in the delivery condition on the other 14-1-2345-88 (samples) |
| ≥1050 |
≥1450 |
≥10 |
≥12 |
≥245 |
| ≥900 |
≥1350 |
≥10 |
≥12 |
≥294 |
| ≥900 |
1150 |
≥8 |
≥10 |
≥245 |
Description mechanical marks
| Name |
Description |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σU |
Limit short-term strength |
| d5 |
Elongation after rupture |
| y |
The relative narrowing |
| KCU |
Toughness |